汽车量子膜施工流程是什么?

发布时间:2020-12-30 作者:济南量子膜专营店 文章来源:http://www.tiekemoshe.com/ 浏览量:

湿烤定型:用热风枪对膜片弧度进行加温,刮板配合热风枪漫漫对弧度做出挤压,由内到外把弧度挤压定型。定型过程中遇弧度较大时,可把一个大弧度分成多个小弧度逐一加温定型。在挤压定型过程中因膜片收缩不足很容易产出打折,应控制好刮板挤压距离,根据膜片收缩程度慢慢挤压平整。边部位置需收缩充分后再挤压。
Wet baking shaping: heating the arc of diaphragm with hot air gun, extruding the arc with scraper and hot air gun, extruding the arc from inside to outside. In the process of shaping, when the radian is large, a large radian can be divided into several small radians and heated one by one. In the process of extrusion, it is easy to produce discount due to insufficient shrinkage of the diaphragm, so it is necessary to control the extrusion distance of the scraper, and slowly extrude and flatten according to the shrinkage of the diaphragm. The edge should be fully contracted before extrusion.
干烤定型:用热风枪对整张膜片各个位置进行加温,由中间往四边左边移动进行加温,一直把膜片上明显的弧度收缩到与玻璃的弧度一致为标准。再把膜片卷起在玻璃外侧喷上安装液,固定膜片按湿烤步骤把膜片刮平、在膜片加温过程中由于膜片收缩不足或收缩过大容易使膜片粘贴过程中造成施工困难,应根据热风枪温度膜片特性与玻璃弧度大小适量的加温使膜片均匀收缩。
济南量子膜
Dry baking and shaping: use a hot-air gun to heat each position of the whole diaphragm, move it from the middle to the left of the four sides for heating, and keep the obvious radian on the diaphragm in line with the radian of the glass. Then roll up the diaphragm, spray installation liquid on the outside of the glass, fix the diaphragm, and scrape it flat according to the wet baking steps. During the heating process of the diaphragm, it is easy to cause construction difficulties in the pasting process due to insufficient or excessive shrinkage of the diaphragm. The diaphragm should be heated appropriately according to the temperature characteristics of the hot air gun and the radian of the glass to make the diaphragm shrink evenly.
干湿结合定型:用热风枪对整张膜片各个位置进行加温,由中间往四边左右移动进行加温,刮板配合热风枪漫漫对加温处进行挤压,挤压过程中应把固定膜片的安装液刮到挤压到的部位以便定型。在加温挤压定型过程中因膜片收缩不足很容易产生打折,应控制好刮板挤压距离,根据膜片收缩程度慢慢挤压平整。边部位置需收缩充分后再挤压。
Dry wet combination shaping: use the hot air gun to heat each position of the whole diaphragm, move from the middle to the four sides for heating, and the scraper with the hot air gun to extrude the heating place for a long time. During the extrusion process, the installation fluid of the fixed diaphragm should be scraped to the extruded part for shaping. In the process of heating extrusion, it is easy to produce discount due to insufficient shrinkage of the diaphragm. Therefore, the extrusion distance of the scraper should be controlled and the diaphragm should be extruded smoothly according to the shrinkage degree of the diaphragm. The edge should be fully contracted before extrusion.
拉抻定型:用手把膜片多余出部分向边上拉平拉直,用热风枪在拉直位置进行加温,使膜片自行左右收缩至玻璃形状。在加温收缩过程中,膜片很容易因温度过高形成收缩过大或烧焦,应该控制热风枪温度与膜片间的距离,观察膜片的收缩变化。
Stretching and shaping: flatten and straighten the surplus part of the diaphragm to the edge by hand, and heat it at the straightening position with a hot air gun to make the diaphragm shrink to the glass shape by itself. In the process of heating shrinkage, the diaphragm is easy to shrink too much or scorch due to too high temperature. The distance between the temperature of the hot air gun and the diaphragm should be controlled to observe the shrinkage change of the diaphragm.